Gan uaim Cruach Feadáin Do Peitriliam scáineadh, GB9948-2006, Sanon Pipe

Cur síos achomair:

Feadáin cruach gan uaim do peitriliam scáineadh , sered as for fumace tubes,heat exchange tubes and 

pipelines in petroleum and refinery plants.High quality carbon structural steel grades are 20g, 

20mng and 25mng;Alloy structural steel grades: 15mog, 20mog, 12crmog,15CrMoG、12Cr2MoG、12CrMoVG,etc


  • Payment: 30% deposit, 70% L/C or B/L copy or 100% L/C at sight
  • Min.Order Quantity: 1 PC
  • Supply Ability: Annual 20000 Tons Inventory of Steel Pipe
  • Lead Time: 7-14 days if in stock, 30-45 days to produce
  • Packing: Black Vanishing, bevel and cap for every single pipe; OD below 219mm need to pack in bundle, and each bundle no exceed 2 tons.
  • Sonraigh Táirge

    CC

    Táirge Clibeanna

    Forbhreathnú

    Caighdeán: GB9948-2006

    Grúpa Grád: 10 , 12CrMo , 15CrMo, 07Crl9Nil0, srl

    Tiús: 1 - 100 mm

    Seachtrach trastomhas (Babhta): 10-1000 mm

    Fad: Seasta fad nó fad randamach

    Rannóg Cruth: Babhta

    Cuir Origin: An tSín

    Deimhniúchán: ISO9001: 2008

     

    Teas Cóireála: Ainéaladh / normalú / Faghartha

    Seachtrach trastomhas (Babhta): 10-1000 Mm

    Feidhmchlár: feadáin mhalartaithe teasa

    Dromchla Cóireála: Mar Riachtanas Chustaiméirí

    Teicníocht: Te Iarchurtha

    Pipe Speisialta: Tiubh Wall Pipe

    Úsáid: feadáin mhalartaithe teasa

    Tástáil: UT / MT

    Iarratais

    Tá Feadáin cruach gan uaim do peitriliam scáineadh infheidhme maidir le feadáin cruach gan uaim do feadáin foirnéise, feadáin mhalartaithe teasa agus píopaí brú sa tionscal peitriceimiceach.

    High quality carbon structural steel grades are 20g, 20mng and 25mng.
    Alloy structural steel grades: 15mog, 20mog, 12crmog
    15CrMoG、12Cr2MoG、12CrMoVG, etc

    príomh Grád

    Grád na cruach struchtúracha carbóin ard-chaighdeán: 10 # , 20 #

    High quality carbon structural steel grades : 20g, 20mng and 25mng

    Alloy structural steel grades: 15mog, 20mog, 12crmog, 15CrMoG、12Cr2MoG,etc

    Comhpháirt Chemical

    Níl

    Grád

    Comhpháirt Chemical%

    C

    Si

    mn

    cr

    Mo

    Ni

    nB

    ti

    V

    Cu

    P

    S

    Ard-chaighdeán cruach carbóin struchtúracha

    10

    0. 07-0.13

    0.17 -0. 37

    0.35 -0.65

    <0.15

    <0.15

    <0. 25

    -

    -

    <0. 08

    <0. 20

    0. 025

    0. 015

    20

    0.17-0. 23

    0.17 -0. 37

    0.35 -0.65

    <0. 25

    <0.15

    <0. 25

    -

    -

    <0. 08

    <0. 20

    0. 025

    0. 015

    Alloy cruach struchtúracha

    12CrMo

    0. 08-0.15

    0.17 -0.37

    0. 40-0. 70

    0. 40-0. 70

    0. 40 -0.55

    <0. 30

    -

    -

    <0. 20

    0. 025

    0. 015

    15CrMo

    0.12 -0.18

    0.17-0. 37

    0.40 -0. 70

    0. 80-1.1

    0. 40-0.55

    <0. 30

    -

    -

    <0. 20

    0. 025

    0. 015

    12CrlMo

    0. 08 -0.15

    0.50 -1. 00

    0. 30-.6

    1.00-1. 50

    0.45 -0.65

    <0. 30

    -

    -

    -

    <0, 20

    0. 025

    0. 015

    12CrlMoV

    0. 08-0.15

    0.17-0. 37

    0. 40-0. 70

    0.90-1.2

    0. 25 -0.35

    <0. 30

    -

    -

    0.15 -0. 30

    <0. 20

    0.025

    0. 010

    12Cr2Mo

    0.08-0.15

    <0. 50

    0. 40-0. 60

    2. 00-2. 50

    0. 90-1.13

    <0. 30

    -

    -

    <0. 20

    0. 025

    0. 015

    12Cr5MoI

    <0.15

    <0. 50

    0.30-0.6

    4. 00-6

    0. 45 -0. 60

    <0. 60

    -

    -

    <0. 20

    0. 025

    0. 015

    12Cr5MoNT

    12Cr9MoI

    <0.15

    0. 25-1. 00

    0. 30-0. 60

    8.00 -10. 00

    0. 90-1.1

    <0. 60

    -

    -

    -

    <0. 20

    0. 025

    0, 015

    12Cr9MoNT

    teas cruach dhosmálta resistant

    07Crl9Nil0

    0. 04-.1

    <1. 00

    <2. 00

    18. 00-20. 00

    -

    8. 00-11

    -

    -

    -

    -

    0. 030

    0. 015

    07Crl8NillNb

    0. 04-.1

    <1. 00

    <2. 00

    17. 00-19. 00

    -

    9.00-12. 00

    8C-1.1

    -

    -

    -

    0. 030

    0. 015

    07Crl9NillTi

    0. 04-.1

    <0. 75

    <2. 00

    17.00-20. 00

    -

    9. 00 ~ 13. 00

    -

    4C-0. 60

    0.03

    0. 015

    022Crl7Nil2Mo2

    <0. 030

    <1. 00

    <2. 00

    16. 00-18. 00

    2. 00-3. 00

    10. 00 -14. 00

    -

    -

    0.03

    0. 015

    Maoin Meicniúil

     Níl teanntachta
    MPa
    Toradh
    MPa
    Elong tar éis briseadh A /% Shork kv2 fuinnimh a ionsú / j Uimhir cruas Brinell
    portráid transver portráid transver
    nach lú ná níos mó ná
    10 335~475 205 25 23 40 27
    20 410~550 245 24 22 40 27
    12CrMo 410~560 205 21 19 40 27 156 HBW
    15CrMo 440~640 295 21 19 40 27 170 HBW
    12CrlMo 415~560 205 22 20 40 27 163 HBW
    12CrlMoV 470~640 255 21 19 40 27 179 HBW
    12Cr2Mo 450 ~ 600 280 22 20 40 27 163 HBW
    12Cr5MoI 415~590 205 22 20 40 27 163 HBW
    12Cr5MoNT 480~640 280 20 18 40 27 -
    12Cr9MoI 460~640 210 20 18 40 27 179 HBW
    12Cr9MoNT 590-740 390 18 16 40 27
    O7Crl9NilO 2520 205 35 187 HBW
    07Crl8NillNb > 520 205 35 - 187 HBW
    07Crl9NillTi > 520 205 35 - - 187 HBW
    022Crl7Nil2Mo2 > 485 170 35 - 187 HBW
    Maidir le cruach le tiús bhalla níos lú ná feadán 5mm ná a dhéanamh ar thurgnamh cruas

    tástáil Riachtanas

    Hydraulic test
    Hydraulic test shall be carried out for steel pipes one by one. The maximum test pressure is 20 MPa. Under the test pressure, the stabilization time shall not be less than 10 s, and leakage of steel pipe is not allowed.
    Flattening test
    Flattening test shall be conducted for steel pipe with outer diameter greater than 22 mm
    Flaring test
    High quality carbon structural steel and stainless (heat-resistant) steel pipes with an outer diameter of not more than 76 mm and a wall thickness of not more than 8 mm shall be subject to expanding test. The flaring test shall be carried out at room temperature. The outer diameter flaring rate of the sample after the top core taper is 60% of the flaring shall meet the requirements of table 7. No cracks or cracks are allowed on the sample after the flaring. According to the requirements of the demander and noted in the contract, the alloy structural steel can also be used for expanding test.
    Nondestructive teste
    The steel pipes shall be subject to ultrasonic flaw detection one by one in accordance with the provisions of GB / T 5777-2008. According to the requirements of the demander, other non-destructive tests can be added after negotiation between the supplier and the demander and indicated in the contract.
    Intergranular corrosion test
    Intergranular corrosion test shall be conducted for stainless (heat-resistant) steel pipe. The test method shall be in accordance with the provisions of Chinese method E in GB / T 4334-2008, and intergranular corrosion tendency is not allowed after the test.
    After negotiation between the supplier and the demander, and noted in the contract, the demander can designate other corrosion test methods.